Features:
Physical Properties:
| Before Curing | Catalyst Components | Base Components |
| Appearance | White putty | Blue putty |
| Mix ratio | 1:1 | |
| Pot life | 2~3 minutes | |
| Curing time(37C) | <30 minutes | |
| After Curing | ||
| Hardness(Shore A) | 40 | |
| Permanent deformation % | <0.2% | |
| Dimensional stability % | <0.25 | |
| Copy details(μm) | <1.5 | |
| tensile Strength Mpa | 2.5 | |
| Temperature stability | 60°C for 1 week | |
| Elongation% | 350 | |
Usage Instruction
1. Under the room temperature, take the same amount of base component (blue) and catalyst component (white).
2. Mix the two components together. It is recommended to use the blue spoon to take the base component and white spoon to take catalyst component.
3. Use your fingertips to mix the two components together and knead for at least 30 seconds until they are mixed completely.
4. Close the lid immediately after usage, the cover can not be interchanged.
Package
Package available in 350g, 500g, 1kg,5kg,10kg, 25kg. sampe available in 100gA+100gB.
Storage
Equine hoof repair silicone putty has a shelf life of 12 month in original package at a cool dry place.
Precautions
1. Do not use natural rubber gloves. It is recommended to use disposable polyethylene plastic gloves.
2. The product contains platinum catalyst, sulfur, phosphorus, amine, etc. will slow down or even stop the curing reaction, and thus it must avoid sulfur, phosphorus, amine, acrylic and acid esters and other chemical products in use.
3. Close the lid tightly and immediately after use, keep it in cool place, and be refrigerated in summer.
4. The temperature has a significant impact on the curing time; the curing reaction will slow down at low temperature, and speed up at high temperature curing speed. It should adjust operation rhythm according to the environment and the finger temperature.
5. It is strictly recommended to use the same amount of base and catalyst. Unequal amount will lead to delayed or accelerated cure.